冷拉方钢规格-冷拉方钢的冷拉工艺分类和参考标准

网站编辑:浙江建鑫型钢科技股份有限公司 │ 发表时间:2020-03-17 

问:冷拉方钢的冷拉工艺是否有不同分类?

Q: Are there different classifications for the cold drawing process of cold drawn square steel?

答:冷拉方钢的冷拉工艺,是有不同分类的,具体来讲,在冷拉时,只用冷拉率或冷拉应力来控制的话,是为单控,而这两个同时进行,是为双控。而且,要知道的是,如果是预应力钢筋的冷拉,则应采用双控,这样比较好。

A:The cold drawing process of cold drawn square steel has different classifications. Specifically, when cold drawing is only controlled by the cold drawing rate or cold drawing stress, it is a single control, and the two are performed simultaneously. Is for dual control . Moreover, it must be known that if it is a cold drawing of prestressed steel bars, dual control should be used, which is better.

问:怎么知道图纸上标注的是冷拉方钢还是热轧方钢?以及结构用冷拉方钢的分类,应参考哪一标准?

Q: How do I know if the drawing is cold drawn or hot rolled? And the classification of cold drawn square steel for structure, which standard should be referred to?

答:对于问题一,一般来讲,如果是没有说明的,是为热轧方钢,有说明的,则是冷拉方钢。如果,还有不懂的话,还可以查阅五金手册。至于,结构用冷拉方钢,在分类上的参考标准,是为《GB/T 3078-2008 优质结构钢冷拉钢材》这一个。

Answer: For question one, in general, if there is no description, it is hot-rolled square steel, and if there is a description, it is cold drawn square steel. If you still don't understand, you can also refer to the hardware manual. As for the cold drawn square steel for structural use, the reference standard for classification is "GB / T 3078-2008 High Quality Structural Steel Cold Drawn Steel".

问:冷拉方钢在使用过程中如果出现摔断或者折断,根本原因是什么?

Q: If the cold drawn square steel is broken or broken during use, what is the root cause?

答:冷拉方钢在使用过程中如果出现摔断或者折断,其根本原因,是该冷拉方钢所使用的原材料有问题,比如,原材料中杂质过多,这时,材料再进行冷拉的话,那么是会出现断裂现象的。

A: If the cold drawn square steel breaks or breaks during use, the root cause is that there is a problem with the raw materials used in the cold drawn square steel, for example, there are too many impurities in the raw material. At this time, the material is cold drawn. If so, then there will be fractures.